Synthesis of Fe-substituted aluminosilicate and aluminogermanate nanotubes
Main Article Content
Abstract
Abstract: In this paper, substitution of Fe3+ for Al3+ in the structure of aluminosilicate and aluminogermanate nanotubes was investigated at various mole ratios of Fe/Al from the mixed Al2O3-Fe2O3-SiO2 (GeO2)-H2O solution in experimental conditions of 2 mM initial concentration and 2 day aging time at 980C. The synthesized products were confirmed and characterized by using FT-IR spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM) and magnetometer. The results indicated that Fe-substituted aluminosilicate and aluminogermanate nanotubes were successfully synthesized with the Fe/Al ratio of the initial solutions up to 2. For both Fe-substituted nanotubes, the paramagnetic property exhibits at room temperature (300 K) and a ferromagnetic property at low temperature (5 K). The materials with new properties appear to have promising practical application in other fields in the future.
Key words: Imogolite, nanotube, substitution, aluminosilicate, aluminogermanateReferences
[2] P.D.G. Cradwick, V.C. Farmer, J.D. Russell, C.R. Masson, K. Wada, and N. Yoshinaga, Imogolite, a hydrated aluminum silicate of tubular structure, Nature Physical Science 240 (1972) 187.
[3] K. Yamamoto, H. Otsuka, S.-I Wada, D. Sohn, A. Takahara, Preparation and properties of [poly(methyl methacrylate)/imogolite] hybrid via surface modification using phosphoric acid ester, Polymer 46 (2005) 12386.
[4] C. Levard, J. Rose, A. Masion, E. Doelsch, D. Borschneck, L. Olivi, C. Domicini, O. Grauby, J.C. Woicik, J.Y. Bottero, Synthesis of large quantities of single-walled aluminogermanate nanotube, Journal of the American Chemical Society 130 (2008) 5862.
[5] S. Mukherjee, V.A. Bartlow, S. Nair, Phenomenology of the growth of single-walled aluminosilicate and aluminogermanate nanotubes of precise dimensions, Chemistry of Materials 17 (2005) 4900.
[6] S. Mukherjee, K. Kim, S. Nair, Short, highly ordered, single-walled mixed-oxide nanotubes assemble from amorphous nanoparticles, Journal of the American Chemical Society 129 (2007) 6820.
[7] S. Imamura, T. Kokuba, T. Yamashita, K. Okamotao, K. Kajiwara, H. Kanai, Shape selective copper loaded imogolite catalyst, Journal of Catalysis 160 (1996) 137.
[8] Y. Arai, M. McBeath, J.R. Bargar, J. Joye, J.A. Davis, Uranyl absorption ans surface speciation at the imogolite-water interface: Self-consistent spectroscopic and surface complexation models, Geochimica et Cosmochimica Acta 70 (2006) 2492.
[9] W.C. Ackerman, D.M. Smith, J.C. Huling, Y.W. Kim, J.K. Bailey, C.J. Brinker, Gas/vapor adsorption in imogolite: a microporous tubular aluminosilicate, Langmuir 9 (1993) 1051.
[10] V.C. Farmer, M.J. Adams, A.R. Fraser, F. Palmieri, Synthetic imogolite: Properties, synthesis, and possible applications, Clay Minerals 18 (1983) 459.
[11] K.S. Ko, W.S. Ahn, Isomorphous substitution of Fe+3 in zeolite LTL, Microporous Materials 9 (1997) 131.
[12] A. Nakahira, S. Nishimura, H. Aritani, S. Ueda, Synthesis of Fe-Substituted Al-Mordenites by Hydrothermal Method, Journal of Materials Science 36 (2001) 1885.
[13] P. Wu, T. Komatsu, T. Yashima, Isomorphous substitution of Fe3 + in the framework of aluminosilicate mordenite by hydrothermal synthesis, Microporous and Mesoporous Materials 20 (1998) 139.
[14] Z. Abidin, N. Matsue, T. Henmi, A new method for nano tube imogolite synthesis, Japanese Journal of Applied Physics 47 (2008) 5079.
[15] S.I. Wada, A. Eto, K. Wada, Synthetic allophane and imogolite, Journal of Soil Science 30 (1979) 347.
[16] S.I. Wada and C. Sakimura, Effect of Calcium, Sodium and Chloride lons on the Growth of Imogolite Tubes as Measured by Gel Forming Property, Clay Science 11 (2000) 115.